Carbide Silicon nigrae varias conjunctas abrasivas facere, ad stridorem et politionem lapidum, ac metallorum et non metallicorum processus cum viribus distrahendis, ut glaucum ferrum, aes, aluminium, lapidem, corium, globulus, etc.
Items | Unitas | Index | |||
Compositio chemica | |||||
Nam abrasives | |||||
Magnitudo | Sic | FC | Fe2O3 | ||
F12-F90 | % | 98.5min | 0.5max | 0.6max | |
F100-F150 | % | 98.5min | 0.3max | 0.8max | |
F180-F220 | % | 987.0min | 0.3max | 1.2max | |
Nam refractarium | |||||
Type | Magnitudo | Sic | FC | Fe2O3 | |
TN98 | 0-1mm 1-3mm 3-5mm 5-8mm 200mesh 325mesh | % | 98.0min | 1.0max | 0.8max |
TN97 | % | 97.0min | 1.5max | 1.0max | |
TN95 | % | 95.0min | 2.5max | 1.5max | |
TN90 | % | 90.0min | 3.0max | 2.5max | |
TN88 | % | 88.0min | 3.5max | 3.0max | |
TN85 | % | 85.0min | 5.0max | 3.5max | |
Liquescens punctum | ℃ | 2250 | |||
Refractio | ℃ | 1900 | |||
Verum density | g/cm*3 | 3.20min | |||
mole densitatis | g/cm*3 | 1.2-1.6 | |||
Mohs duritiem | --- | 9.30min | |||
Color | --- | nigreos |
Carbide Silicon nigrum ex fusione vicus arenae, anthracites et silicae qualitatem in fornace electrica resistente producitur.SiC caudices cum structura crystalli maxime compacta iuxta nucleum diligenter selectae sunt ut materias rudis.Per acidum perfectum et aquam lavacrum post contritionem, contentus carbonis ad minimam redactus ac deinde crystallis puris splendentibus obtinetur.Res fragilis et acuta, et certas conductionis et scelerisque conductionis habet.
Habet stabilia chemicae proprietates, coefficientem conductivity altam, humilem coëfficientem expansionis scelerisque et excellentis indumenti resistentiae, et ad applicationes refractarias et stridor aptas.