Alumina monocrystallina apta est vitrificatis, resinatis et Flexilis religata stridentibus rotae, stridor altae vanadium, altum celeritatem ferri, austeniticum chalybem immaculatum, calo renitens mixturae chalybis et titanii mixturae ferri, praesertim ad stridorem operum comburentium et siccum. molere.
Items | Unitas | Index | Typical | |
Compositio chemica | Al2O3 | % | 99.00min | 99.10 |
SiO'2 | % | 0.10max | 0.07 | |
Fe2O3 | % | 0.08max | 0.05 | |
TiO2 | % | 0.45max | 0.38 | |
Compressive fortitudo | N | 26min | ||
Fortitudo | % | 90.5 | ||
Liquescens punctum | ℃ | 2250 | ||
Refractio | ℃ | 1900 | ||
Verum density | g/cm3 | 3.95min | ||
Mohs duritiem | --- | 9.00min | ||
Color | --- | Cinereo albo / Blue | ||
Gradus Abrasive | FEPA | F12-F220 |